VM 25S 80

VM25S80.png

Super Duplex VM 25S 80 is a Corrosion Resistant Alloy. It is called "Super Duplex" because of its improved corrosion resistance to H2S. It is iron based plus main alloying elements Cr, Ni and ​Mo. The PRE is above 40. Structure is Duplex (austenite and ferrite). VM 25S 80 is delivered in solution annealed conditions.

​APPLICATIONS

VM 25S 80 is recommended when pCO​2 is above 2psi / 0.14bar and high temperature up to 482°F / 250°C. Chlorine is limited to 120,000ppm. It can be used with some amount of H2S (3psi – 0.2bar). Partial pressure H2S acceptable is governed by temperature.

VM 25S 80 can be used as tubing or casing.

​PERFORMANCES

VM 25S 80 has been tested from room to high temperature for SCC and SSC with different levels of H2S.​

​Typical C​hemical composition

UNS​CCrNiMo

 N

 PRE

S32760​0,03 max24 - 266 - 83 - 4​0.2 - 0.8≥ 40

​PRE=Pitting Resistance Equivalent = %Cr + 3.3 %Mo + 1.65 % W + 16 % N

​​D​ensity = 7.82kg/dm3

MECHANICAL PROPERTIES 

​​In solution annealed condition​

Yield Strength
ksi (M​Pa)
Ultimate Tensile Strength
ksi (MPa)
Elongation
%
Hardness
HRC
Min.Max.Min.Min.Max.​​
80
(552)
105
(724)
110
(758)
25%28​

Control hardness through wall   ​

​Less than 0.357"
(Less than 9.00mm)
​0.354" to ​0.499"
(9.00 to 12.69mm)
​0.500" to ​0.759" 
​(12.70 to 19.04mm)
​​0.750" to 0.999"
(19.05 to 25.39mm)
1.​000" and above
(25.40mm and above)

​3.0

3.0

​4​.0​

5.0

6.0​​​

PHYSICAL PROPERTIES

Physical properties & ​evolution with temperature


Characteristic ​​
Unit ​​Tem​peratu​re (°C) ​ ​ ​ ​ ​
25​50100​150200​ 250
Yield Strength
derating
%​1.0000.9430.8710.8190.7810.751
Ultimate Tensile Strength
derating
%1.0000.9720.9320.9020.8800.862
Thermal conductivityW m-1 K-1​14.3714.6614.9717.1517.8018.44
Thermal diffusivityx 10-6 m²  s-1​3.683.763.924.094.254.42
Thermal expansionx 10-6 / deg. C-13.213.413.513.713.9
Poisson's ratio-​      
Young's modulusGPa194.9193.1190.0186.9183.6180.7
Resistivitynano Ohm.m89691294397310041034
Specific heat capacityJ.g-1.K-10.500.500.490.540.540.54​​​

FIELD RECORDS 

The product is used in the following areas:

  • ​North Africa: e.g. ​3 1/29.2VAM TOP®, 4 1/2" 12,6# VAM TOP®
  • South America: e.g. 4 1/2" 12.6# VAM TOP®
  • ​North Sea: e.g. 4 1/212.6VAM TOP® ​HTTM.

​STORAGE & HANDLING RECOMMENDATION

Avoid pollution by contact from carbon or low alloy steel (pipe or parts).

Avoid atmospheric pollution with iron (e.g. concrete plant).