VM G3 110

VM G3 110.png

​V​M G3 110 is an austenitic Corrosion Resistant Alloy nickel based. The main alloying elements are Ni, Cr and Mo. VM G3 110 is delivered in cold work condition. It can be hardened by drawing or pilgering.

​APPLICATIONS​

VM G3 110 is recommended in very severe environments with CO2, H2S, chlorine and possibly presence of native sulfur. The VM G3 110 is designed for resistance to very high temperature. VM G3 110 can be used as tubing or casing.

​PERFORMANCES

VM G3 110 has been tested from room to high temperature for SCC with different levels of H2S.

​​Typical Chemical composition

​UNS​ C​ Cr Fe Ni Mo
N06985 0,015 max 21 - 23
18 - 21
bal
6 - 8

Density = 8.31kg/dm3

MECHANICAL PROPERTIES

​After cold work

​Yield Strength 

ksi (​MPa)​

​Ultim​ate Tensile

Strength ksi (MPa)  

​Elongation
​%   
Mean ​Hardness
HRC 
Min.
Max.
Min. ​Min.​
Max.
​110  
(758) 
130
(896)
115
(793)
11% ​​35

Control hardness through wall   ​

​Less than 0.357"
(Less than 9.00mm)​
​0.354" to 0.499"
(9.00 to 12.69mm)
​0.500" to 0.759" 
(12.70 to 19.04mm)
​0.750" to 0.999"
(19.05 to 25.39mm)
​1.000" and above
(25.40mm and above)
​3.0 ​4.0 ​5.0 ​6.0 ​​6.0

STORAGE & HANDLING RECOMMENDATION

Avoid pollution by contact from carbon or low alloy steel (pipe or parts).

Avoid atmospheric pollution with iron (e.g. concrete plant).

Please refer to the VAM® BOOK​.​​

 
 